Demonstration of Chromatic Dispersion Compensation Fibre Using Square Hole PCF

Abstract

N recent years PCFs made of silica and air hole has provided a new approach for dispersion compensation. For dispersion compensating fibers, large negative dispersion D(ps/km-nm)is required. To maintain the flat and zero dispersion in photonic crystal fiber (PCF) different air hole diameter and different pitches has been introduced. These differences in diameter and pitches gives different dispersion graphs and after comparison we get that design which has lowest dispersion among them. This paper proposes a new geometry of PCFs which uses ‘square’ holes instead of circular holes which gives large negative dispersion without high doping.

• square hole PCF
• Negative dispersion

Аннотация (на русском)

Демонстрация компенсации хроматической дисперсии с использованием ФКВ с квадратными отверстиями

В последние годы ФКВ из кварцевого стекла с микроотверстиями для воздуха обеспечили новые подходы. Для компенсации дисперсии волокна требуется большая отрицательная дисперсия D(ps/км-нм). Для получения нулевой дисперсии в фотонно-кристаллических волокнах (ФКВ) применяется различный диаметр отверстий для воздуха и различный шаг между ними. Эти различия в диаметре и шаге образуют различные профили дисперсии, и после сравнения, мы выбираем ФКВ с наименьшей дисперсией. В настоящей статье предлагается новая геометрия ФКВ, которые использует квадратные микроотверстия вместо круглых, что дает большую отрицательную дисперсию с относительно малым затуханием.

For citation

References

1. Bjarklev A, Broeng J, Bjarklev AS. Photonic crystal fibers. Dordrecht: Kluwer Academic Publishers; 2003.
2. Knight JC, Birks TA, Russell PSJ, Atkin DM. All-silica singlemode optical fiber with photonic crystal cladding. Opt Lett 1996;21:1547-9.
3. Broeng J, Mogilevstev D, Barkou SE, Bjarklev A. Photonic crystal fibers: a new class of optical waveguides. Opt Fiber Technol 1999;5:305-30.
4. Reeves WH, Knight JC, Russell PStJ. Demonstration of ultraflattened dispersion in photonic crystal fibers. Opt Express2002;10:609-13.
5. T. A. Birks, D. Mogilevtsev, J. C. Knight, and P. St. J. Russell, “Dispersion compensation using single-material fibers,” IEEE Photon. Technol. Lett., vol. 11, pp. 674-676, June 1999.
6. A. Ferrando, E. Silvestre, J. J. Miret, J. A. Monsoriu, M. V. Andres, and P. St. J. Russell, “Designing a photonic crystal fiber with flattened chromatic dispersion,” Electron. Lett., vol. 35, pp. 325-327, 1999.
7. M. J. Gander, R. McBride, J. D. C. Jones, D. Mogilevtsev, T. A. Birks, J. C. Knight, and P. St. J. Russell, “Experimental measurement of group velocity dispersion in photonic crystal fiber,” Electron. Lett., vol. 35, pp. 63-64, 1999.
8. J. K. Ranka, R. S.Windeler, and A. J. Stentz, “Visible continuum generation in air-silica microstructure optical fibers with anomalous dispersion at 800 nm,” Opt. Lett., vol. 25, pp. 25-27, 2000.
9. W. J. Wadsworth, J. C. Knight, A. Ortigosa-Blanch, J. Arriaga, E. Silvestre, and P. St. J. Russell, “Soliton effects in photonic crystal fibers at 850 nm,” Electron. Lett., vol. 36, pp. 53-55, 2000.